Compressive deformation of wood impregnated with low molecular weight phenol formaldehyde (PF) resin III: effects of sodium chlorite treatment
Journal of Wood Science volume 51, pages 234–238 (2005)
Abstract
To obtain high-strength phenol–formaldehyde (PF) resin-impregnated compressed wood at low pressing pressure, we investigated the effects of sodium chlorite (NaClO2) treatment on wood prior to low molecular weight PF resin impregnation. Sawn veneers of Japanese cedar (Cryptomeria japonica) were treated with 2% aqueous NaClO2 solution at 45°C for 12 h to remove lignin, and the process was repeated up to four times, resulting in weight loss of 21%. NaClO2 treatment has shown considerable potential for high compression of PF resin-impregnated wood at low pressing pressure, especially after adding moisture to a content of 10%–11%. This deformation is further enhanced during pressure holding by creep deformation. The density, Young’s modulus, and bending strength of PF resin-impregnated veneer laminated composites that were treated with NaClO2 four times and compressed at 1 MPa, reached 1.15 g/cm3, 27 GPa, and 280 MPa, respectively. The values in untreated PF resin-impregnated wood reached 0.8 g/cm3, 16 GPa, and 165 MPa, respectively.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shams, M., Yano, H. & Endou, K. Compressive deformation of wood impregnated with low molecular weight phenol formaldehyde (PF) resin III: effects of sodium chlorite treatment. J Wood Sci 51, 234–238 (2005). https://doi.org/10.1007/s10086-004-0638-y
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10086-004-0638-y