Table 4 Mulberry scrimber mechanical and physical property evaluation

From: Effects of density and resin content on the physical and mechanical properties of scrimber manufactured from mulberry branches

 

Density (g/cm3)

MOR (MPa)

MOE (MPa)

SS-PE (MPa)

SS-PA (MPa)

24 h-TS (%)

Mulberry scrimber

1.02

98.1

11,920

11.6

9.5

5.3

GB/T 20241-2006

/

/

/

6.5(65 V-55H)

5.5(65 V-55H)

12

GB/T 21128-2007

/

90 (A)

9,000(A)

/

/

/

  1. MOR modulus of rupture, MOE modulus of elasticity, SS-PE shear strength perpendicular to the panels, SS-PS shear strength parallel to the panels, 24 h-TS 24 h thickness swelling