Official Journal of the Japan Wood Research Society
Properties | D (1)12 (g cm−3) | D b (2) (g cm−3) | E (3)c‖ (MPa) | σ (4)c║ (MPa) | σ (5) t‖ (MPa) | σ (6)e║ (MPa) | σ (7)s (MPa) | σ (8)c⊥ (MPa) | σ (9)c,p⊥ (MPa) | σ (10) t⊥ (MPa) | σ (11)e⊥ (MPa) |
---|---|---|---|---|---|---|---|---|---|---|---|
Clone GT 1 | |||||||||||
Arithmetic mean | 0.662 | 0.541 | 12.61 | 49.83 | 76.45 | 48.15 | 9.43 | 11.24 | 5.94 | 4.23 | NA |
CV (%) | 7.5 | 4.4 | 11.5 | 7.5 | 21.3 | 8.9 | 18.7 | 8.5 | 15.2 | 25.9 | NA |
Median* | 0.663a | 0.535a | 12.75a | 48.64a | 78.43a | 48.03a | 8.89a | 11.49a | 6.14a | 3.97a | NA |
Clone RRIM 600 | |||||||||||
Arithmetic mean | 0.678 | 0.553 | 9.92 | 43.53 | 70.92 | 44.39 | 9.60 | 11.38 | 6.16 | 4.04 | 21.44 |
CV (%) | 4.5 | 6.3 | 10.4 | 8.6 | 25.6 | 16.7 | 17.4 | 16.9 | 14.8 | 15.3 | 9.5 |
Median* | 0.681a | 0.550a | 9.47b | 42.44b | 74.83a | 47.70a | 9.29a | 11.72a | 6.05a | 4.11a | 22.03 |