Official Journal of the Japan Wood Research Society
k GH-erythro /k GH-threo | k GG-erythro /k GG-threo | k GS-erythro /k GS-threo | k SG-erythro /k SG-threo | k SS-erythro /k SS-threo | ||||||
---|---|---|---|---|---|---|---|---|---|---|
130 °C | 3.7 | 4.3 | 6.0 | 5.2 | 7.9 | |||||
140 °C | 3.6 | 4.2 | 5.4 | 5.0 | 5.9 | |||||
150 °C | 3.4 | 4.1 | 5.0 | 4.7 | 4.5 | |||||
160 °C | 3.3 | 4.0 | 4.6 | 4.6 | 3.5 | |||||
170 °C | 3.1 | 4.0 | 4.3 | 4.4 | 2.7 |
k GG/k GH | k GS/k GH | k SS/k SG | k SG/k GG | k SS/k GS | ||||||
---|---|---|---|---|---|---|---|---|---|---|
erythro | threo | erythro | threo | erythro | threo | erythro | threo | erythro | threo | |
130 °C | 3.5 | 3.5 | 15.6 | 9.8 | 5.1 | 3.3 | 1.5 | 1.2 | 1.7 | 1.2 |
140 °C | 3.4 | 2.8 | 13.0 | 8.5 | 4.0 | 3.4 | 1.4 | 1.2 | 1.4 | 1.3 |
150 °C | 3.3 | 2.7 | 11.0 | 7.5 | 3.2 | 3.4 | 1.3 | 1.1 | 1.3 | 1.4 |
160 °C | 3.2 | 2.6 | 9.3 | 6.6 | 2.6 | 3.4 | 1.2 | 1.1 | 1.1 | 1.5 |
170 °C | 3.1 | 2.5 | 8.0 | 5.9 | 2.1 | 3.5 | 1.2 | 1.1 | 1.0 | 1.5 |
k G′G/k G′H | k G′S/k G′H | k S′G/k S′H | k S′S/k S′H | k S′S/k S′G | ||||||
---|---|---|---|---|---|---|---|---|---|---|
130 °C | 3.5 | 6.7 | 2.1 | 6.2 | 2.9 | |||||
140 °C | 3.1 | 5.9 | 2.1 | 5.6 | 2.7 | |||||
150 °C | 2.7 | 5.2 | 2.1 | 5.2 | 2.5 | |||||
160 °C | 2.4 | 4.6 | 2.0 | 4.8 | 2.3 | |||||
170 °C | 2.1 | 4.1 | 2.0 | 4.4 | 2.2 |
k S′H/k G′H | k S′G/k G′G | k S′S/k G′S | ||||||||
---|---|---|---|---|---|---|---|---|---|---|
130 °C | 1.4 | 0.8 | 1.3 | |||||||
140 °C | 1.4 | 0.9 | 1.3 | |||||||
150 °C | 1.3 | 1.0 | 1.3 | |||||||
160 °C | 1.3 | 1.1 | 1.4 | |||||||
170 °C | 1.3 | 1.3 | 1.4 |