Official Journal of the Japan Wood Research Society
Table 2 Average MOR, MOE, and MC of the specimen before and after rupture load test
Temperature (°C) | Surface-layer | Inner-layer | ||||||
|---|---|---|---|---|---|---|---|---|
MOR (MPa) | MOE (GPa) | MC (%) | MOR (MPa) | MOE (GPa) | MC (%) | |||
Before | After | Before | After | |||||
20 | 9.76 (1.42) | 0.47 (0.10) | 11.9 (0.7) | 13.6 (0.5) | 13.28 (1.11) | 0.95 (0.21) | 10.8 (1.2) | 12.9 (0.4) |
65 | 7.53 (1.43) | – | 10.5 (1.2) | 13.5 (2.0) | 12.53 (2.45) | – | 10.7 (1.4) | 12.5 (0.8) |
80 | 7.48 (1.39) | – | 10.0 (0.4) | 10.7 (0.4) | 11.36 (2.13) | – | 9.6 (0.4) | 10.2 (0.3) |
95 | 4.55 (1.01) | – | 10.3 (0.8) | 9.9 (0.8) | 9.14 (1.80) | – | 9.5 (0.9) | 9.4 (0.9) |