Chemical composition | CaO | SiO2 | Al2O3 | Fe2O3 | Alkali | MgO |
---|---|---|---|---|---|---|
[mass %] | 58.9 | 19.2 | 5.5 | 3.2 | < 1 | 1.7 |
Specific surface area | Specific weight | Compressive strength | ||||
419 m2/kg | 3172 kg/m3 | 59 MPa | ||||
Initial setting time | Granulometric composition | |||||
155–187 min | Shown in Fig. 1 |