Official Journal of the Japan Wood Research Society
Sources | \(E_{L}\) | \(E_{R}\) | \(E_{T}\) | \(G_{RT}\) | \(G_{TL}\) | \(G_{LR}\) | \(\nu _{RT}\) | \(\nu _{TL}\) | \(\nu _{LR}\) | d | H |
---|---|---|---|---|---|---|---|---|---|---|---|
 | (GPa) | (GPa) | (GPa) | (MPa) | (MPa) | (MPa) |  |  |  |  | (%) |
[133] | 11.4 | 0.94 | 0.70 | 200 | 1615 | 1350 | 0.58 | 0.03 | 0.32 | 0.49-0.54 | 11.8-13.5 |
[136] | 15.1 | 1.91 | 1.01 | 280 | 1340 | 1480 | 0.586 | 0.051 | 0.471 | / | / |
[137] | / | 1.1 | / | / | / | / | / | / | / | / | / |
[134] Iosipescu Test | / | / | / | 286 | 1220 | 1410 | / | / | / | 0.578-0.589 | 10-12 |
[134] Off-axis Shear Test | / | / | / | / | 1040 | 1110 | / | / | / | 0.538-0.582 | 10-12 |
[135] Arcan Test | / | / | / | 239 | 1090 | 1330 | / | / | / | 0.608-0.660 | 11 |
[138] Measure 1 | 13.2 | / | / | / | / | / | / | / | 0.46 | 0.46 | / |
Measure 2 | 15.7 | / | / | / | / | / | / | / | 0.35 | 0.60 | / |
Table 4.25 | 16.11-17.77 | / | / | / | / | / | / | / | / | 0.635-0.725 | / |
[139]* | / | 1.4-2.6 | 0.4-1.5 | 110-333 | / | / | 0.53-0.95 | / | / | 0.58 | / |
[57] | 3-15 | / | / | / | / | / | / | / | / | / | / |